Potassium carbonate with carbon supports and catalysts with elemental alkali metal

ABSTRACT

Catalyst supports, catalysts, method for the preparation thereof, and dimerization processes therewith are provided. Catalyst supports consist essentially of potassium carbonate with a crush strength of at least 5 pounds and at least one carbonaceous compound. Catalysts consist essentially of at least one elemental alkali metal deposited on the novel catalyst supports. Optionally, the catalysts further consist essentially of at least one promoter selected from the group consisting of elemental copper, elemental cobalt, and finely divided stainless steel.

This application is a division of application Ser. No. 747,747, filed June 24, 1985, now U.S. Pat. No. 4,595,787.

This invention relates to catalysts. In one aspect, this invention relates to the preparation of catalysts. In another aspect, this invention relates to catalysts active for the dimerization of olefins. In yet another aspect, this invention relates to a process for the dimerization of olefins.

BACKGROUND

It is known in the art to employ supported alkali metal catalysts for such conversions as propylene dimerization. In addition, the use of alkali metal carbonates as catalyst supports is known in the art. However, such catalysts as alkali metals supported on alkali metal carbonate supports do not always give high yields of the desired products, either due to low feed conversion, low product selectivity or both. In addition, the use of alkali metal carbonates alone as catalyst supports has been disadvantageous, especially in fixed bed operations for the reason that the supports do not have sufficient strength. Alternatively, prior art olefin dimerization catalyst systems have been limited to use in batch-type reaction due to the catalyst solubility or the fragile nature of prior art particulate catalysts.

OBJECTS OF THE INVENTION

An object of this invention, therefore, is catalyst supports which are well suited for use in fixed bed operation.

Another object of the invention is catalysts for the dimerization of dimerizable olefins which are well suited for use in fixed bed operation.

Yet another object of this invention is a method for the preparation of the above mentioned catalysts.

Still another object of this invention is catalysts and processes for the dimerization of dimerizable olefins which produce dimerized product in high yield and with high selectivity.

These and other objects of the invention will become apparent from the disclosure and claims herein provided.

STATEMENT OF THE INVENTION

In accordance with the present invention, I have discovered that pelleting potassium carbonate in the presence of a carbonaceous compound, and thereafter oxidatively removing a portion of the carbonaceous compound provides a rugged support with high crush strength and which allows for the preparation of elemental alkali metal dimerization catalysts having high dimerization activity.

DETAILED DESCRIPTION OF THE INVENTION

In accordance with the present invention, a method for producing a catalyst support is provided which comprises first pelletizing a mixture of potassium carbonate and about 0.1-10 weight percent of at least one carbonaceous compound, then heating the pelletized product in an oxygen-containing atmosphere under conditions suitable to oxidize in the range of about 10-90% of the carbonaceous compound. The resulting support can thereafter be contacted in an oxygen-free atmosphere with at least one elemental alkali metal at a temperature sufficient to cause the alkali metal to melt, thereby producing a dimerization catalyst.

In accordance with another embodiment of the present invention, a support having a particle size of at least about 300 microns and a crush strength of at least about 5 pounds is provided consisting essentially of potassium carbonate and about 0.09-9 weight percent of at least one carbonaceous compound wherein the concentration of said carbonaceous compound is substantially less at the surface of said support than in the interior portions of said support. This differential content of carbonaceous compound between the support interior and exterior portions results from the partial oxidation of the support which is carried out after the potassium carbonate is pelletized. In a particular aspect of this embodiment, novel dimerization catalysts are provided consisting essentially of the above described support and about 0.1 to 20 weight percent of at least one alkali metal.

In accordance with a further embodiment of the invention, an improved process is provided for the dimerization of dimerizable olefins with catalysts prepared as described hereinabove.

The potassium carbonate support of the present invention is prepared by first pelletizing a mixture of potassium carbonate and about 0.1-10 weight percent of at least one carbonaceous compound. Potassium carbonate is readily available commercially and any such source is suitable. For purposes of this disclosure, the term "carbonaceous compound" is intended to include various forms of the element carbon, including, but not limited to carbon black, charcoal, coconut charcoal, amorphous graphite, crystallite graphite, and the like, as well as mixtures of any two or more thereof. Finely divided graphite is presently preferred because it is useful both as a die lubricant for the pelleting process and it imparts dramatically improved activity to the finished dimerization catalyst.

The actual pelleting operation can be carried out in any suitable pelleting apparatus. If desired, lubricants such as stearic acid, rosin, hydrogenated coconut oil, and the like can also be added to the potassium carbonate-carbonaceous compound mixture to be pelleted.

The pelleted support can then be subjected directly to the next step, i.e., the partial oxidation step, or can optionally be ground into smaller size particles if desired for subsequent use.

The pelleted support, either as the pellets or as smaller crushed particles, is then heated in an oxygen-containing atmosphere under conditions suitable to oxidize in the range of about 10-90% of the carbonaceous compound. While suitable oxidation conditions can be readily determined by those of skill in the art, temperatures in the range of about 200°-900° C. for a time in the range of about 0.1 to 48 hours are generally suitable. It is recognized by those of skill in the art that longer contact times will generally be appropriate at lower treatment temperatures and conversely, shorter contact times will be appropriate at higher treatment temperatures. Presently preferred treatment temperatures are in the range of about 250°-600° C. for a treatment time of about 0.5 to 6 hours. Such treatment conditions will be expected to cause oxidation of at least 20% of the carbonaceous compound, but less than about 80% of the carbonaceous compound. Most preferably, treatment conditions which cause the oxidation of about 30 to about 70% of the carbonaceous compound will be employed. As a result of this partial oxidation of the pelleted support, the concentration of carbonaceous compound remaining on the surface of the support is substantially less than the concentration of carbonaceous compound remaining in the interior portions of the support.

The pelleted, oxidized support can then be subjected directly to the next step, i.e., treatment with at least one catalytically active material, or can optionally be ground into smaller size particles if desired for subsequent use.

The pelleted support prepared as described hereinabove is very useful for the preparation of potassium carbonate supported catalysts because of the high crush strength of the resulting pellets or ground particulate material derived therefrom. Thus, pellets prepared in accordance with the present invention have crush strengths of at least about 5 pounds. In most preparations, pellets having crush strengths of at least about 20 pounds are obtained, with crush strenght as high as 50 pounds or higher possible. Due to the high crush strength of the potassium carbonate supports prepared as described above, the pellets are useful in fixed bed operations directly as obtained from the pelleting process or alternatively the pellets can be crushed to smaller particle sizes if desired for more efficient packing of the particulate material in a fixed catalyst bed. For such purposes, the pelleted potassium carbonate support of the invention retains its high crush strength for a particulate matter as small as about 300 microns. It is of course recognized by those of skill in the art that pellets of most any desired size can be prepared, e.g., 1/8 inch, 3/16 inch, 1/4 inch, 3/8 inch etc.

DIMERIZATION CATALYSTS

Dimerization catalysts employed in the practice of this invention consist essentially of the potassium carbonate support prepared as described above, at least one elemental alkali metal and, optionally, one or more of the following promoters:

elemental copper,

elemental cobalt,

finely divided stainless steel,

and mixtures of two or more thereof. It should be recognized, however, that the catalysts of the invention can contain additional components which do not adversely affect the catalyst performance, such as, for example, pigments, dyes, processing aids, inert fillers, binders and the like.

The alkali metals contemplated to be within the scope of the invention include lithium, sodium, potassium, rubidium and cesium. While the proportion of alkali metal combined with the potassium carbonate support can vary appreciably, generally at least about one weight percent of alkali metal based on the total weight of treated support will be employed. Generally, about 1 to about 20 wt. % alkali metal will be employed with about 2 to about 15 wt. % preferred. An alkali metal loading of about 3 to about 10 wt. % based on the total weight of treated support is most preferred for most efficient use of reagents, high catalyst activity and selectivity, ease of catalyst preparation and the like. Similarly, potassium is the preferred alkali metal due to its ready availability as well as ease and safety in handling.

The proportion of promoter, when employed, which can be combined with the potassium carbonate support can vary appreciably, but generally, at least one weight percent of that promoter based on the total weight of treated support will be employed. The following amounts are provided for additional guidance:

    ______________________________________                                                Loading, Wt. %                                                          Promoter Broad       Intermediate                                                                              Preferred                                      ______________________________________                                         Cu       1-30        3-20       5-12                                           Co       1-50        3-25       5-15                                           SS       1-80        3-60       5-50                                           ______________________________________                                    

The general procedure for preparation of the dimerization catalysts of the invention involves contacting the pelletized support following the oxidation step with at least one elemental alkali metal in an oxygen-free atmosphere, such as, for example N₂, Ar or the like, at a temperature sufficient to cause the alkali metal to melt. The contacting is preferably carried out with vigorous stirring to ensure even distribution. Those of skill in the art recognize that suitable temperature for the contacting step will vary with the particular alkali metal employed. For example, with elemental potassium, temperatures in the range of about 80° C. to 100° C. are preferred, while with elemental sodium, temperatures in the range of about 100° C. to 140° C. are preferred.

While the alkali metal treated support is maintained at or above about 80° C., any promoter such as for example elemental copper, can, if desired, be gradually added while the treated catalyst is continuously stirred. Catalyst is then ready to be charged to the reactor.

Optionally, the catalyst, once elemental alkali metal and any desired promoters have been deposited thereon, can be subjected to a subsequent heating step to ensure as uniform a distribution as possible of the various promoting metals on the surface of the potassium carbonate support. Thus, the finished catalyst can be subjected to a temperature in the range of at least about 150° C. for a time in the range of about 0.1 to 4 hours. A temperature in the range of about 250°-400° C. for a time in the range of about 0.5-2 hours is presently preferred.

REACTANTS

Reactants applicable for use in the process of the invention are olefinic compounds which can (a) self-react, i.e., dimerize, to give useful products such as, for example, the self-reaction of propylene gives 4-methyl-1-pentene; and/or (b) olefinic compounds which can react with other olefinic compounds, i.e., co-dimerize, to give useful products such as, for example, co-dimerization of ethylene plus propylene gives 1-pentene, co-dimerization of ethylene and 1-butene gives 3-methyl-1-pentene and so forth. As used herein, the term "dimerization" is intended to include "co-dimerization" as defined above.

Suitable dimerizable olefinic compounds are those compounds having from about 3 to about 30 carbon atoms and having at least one olefinic double bond and at least one allylic hydrogen atom, i.e., at least one hydrogen atom attached to a carbon atom adjacent to a double-bonded carbon atom. Exemplary compounds include, but are not limited to, acyclic and cyclic olefins such as for example propylene, 1-butene, 2-butene, isobutylene, 1-pentene, 2-pentene, 1-hexene, 2-hexene, 3-hexene, 1-heptene, 2-heptene, 3-heptene, the four normal octenes, the four normal nonenes and so forth; 3-methyl-1-butene, 2-methyl-2-butene, 3-methyl-1-pentene, 3-methyl-2-pentene, 4-methyl-1-pentene, 4-methyl-2-pentene, tetramethylethylene and the like; cyclopentene, cyclohexene, methylcyclopentene, methylcyclohexene, and the like and mixtures of any two or more thereof.

Suitable co-dimerizable olefinic compounds are those compounds having from about 2 to about 30 carbon atoms, including all the compounds contemplated within the scope of "dimerizable" olefinic compounds as indicated above. In addition, olefinic compounds which do not have at least one allylic hydrogen atom are also included within the scope of co-dimerizable olefins. Exemplary compounds in addition to those indicated above, include, but are not limited to ethylene, 3,3-dimethyl-1-butene, ditertiarybutyl ethylene and the like and mixtures of any two or more thereof.

The compounds indicated above as dimerizable olefinic compounds are capable of undergoing both self-reaction, i.e., dimerization, and cross-reaction, i.e., co-dimerization, with other members of the same group or with those compounds designated as co-dimerizable. The co-dimerizable compounds which do not have at least one allylic hydrogen may be capable of isomerization to form an olefin having an allylic hydrogen under the reaction conditions employed. If such isomerization is not possible, then those non-isomerizable, co-dimerizable compounds which do not have at least one allylic hydrogen must, however, be contacted with at least one of the "dimerizable" compounds in order to facilitate the desired co-dimerization reaction. In other words, the co-dimerizable compounds which do not have at least one allylic hydrogen atom and are not capable of isomerization to produce an olefin having at least one allylic hydrogen are therefore not capable of reacting with themselves under the reaction conditions employed for the dimerization reaction.

REACTION CONDITIONS

The dimerization reaction of the invention can be carried out using either batch or continuous types of operation, although the catalysts of the invention are particularly well suited for continuous, i.e., fixed bed, operation. Suitable equipment such as for example autoclaves, tubular reactors and the like as are well known in the art can be employed. No special materials of construction are required so that steel, stainless steel, glass-lined reactors, or the like can be employed.

The reaction temperature can vary depending on the catalyst and feed(s) employed. Typically, a temperature range of about 50° to about 250° C. is suitable. Temperatures of about 80° to about 200° C. are preferred with a range of about 120° to about 160° C. most preferred because optimum reaction rates are obtained with minimum by-product formation.

The dimerization reaction can be carried out by contacting the dimerizable olefins with catalyst in the liquid phase or the gas phase, depending on the structure and molecular weight of the olefin, as well as reaction temperature and pressure employed. Pressure during the dimerization reaction can vary between wide limits. In general, higher pressures favor the progress of the reaction. Thus, pressures of atmospheric up to about 10,000 psig and higher are suitable. Preferably, pressures of about 100 to about 5,000 psig are employed, with pressures of about 1000 to about 4000 psig most preferred in order to achieve a good balance between reaction rate and minimize equipment and operating costs necessitated by very high reaction pressures.

If the reaction is carried out in the liquid phase, solvents or diluents for the reactants can be used. Saturated aliphatic hydrocarbons, e.g., pentane, hexane, cyclohexane, dodecane; aromatic compounds, preferably those without an alpha-hydrogen (which would be capable of undergoing alkylation under the reaction conditions) such as benzene and chlorobenzene are suitable. If the reaction is carried out in the gaseous phase, diluents such as aliphatic hydrocarbons, for example methane, ethane and/or substantially inert gases, e.g., nitrogen, argon, can be present.

The contact time required for the dimerization reaction depends upon several factors such as for example the activity of the catalyst, temperature, pressure, structure of the reactants employed, level of conversion desired, and the like. The length of time during which the dimerizable olefinic compounds are contacted with catalyst can vary conveniently between about 0.1 seconds and about 24 hours although shorter and longer contact times can be employed. Preferably, times of about one minute to about 5 hours are employed. Where reaction is carried out in continuous fashion, it is convenient to express the reactant/catalyst contact time in terms of weight hourly space velocity (WHSV), i.e., the ratio of the weight of reactant which comes in contact with a given weight of catalyst per unit time. Thus, a WHSV of about 0.1 to about 10 will be employed. A WHSV of about 0.5 to about 5 is preferred, with about 1 to about 4 WHSV most preferred for optimum catalyst productivity.

PRODUCTS

The olefinic products of the invention have established utility in a wide variety of applications such as for example as monomers for use in the preparation of homopolymers, copolymers, terpolymers, e.g., as the third component of ethylene-propylene terpolymers useful as synthetic elastomers, and the like.

A further understanding of the present invention and its advantages will be provided by reference to the following examples.

EXAMPLE I Catalyst Preparation

Catalyst support was prepared by pelleting commercially available anhydrous potassium carbonate on a Stokes-Pennwalt Model 900-511-6 Eureka Tabletting Machine. Pellets (1/8") were prepared and used directly, or crushed and sieved to recover a desirable particle size. The potassium carbonate was admixed with varying amounts of a die lubricant prior to subjecting to the pelleting process.

After pelleting, the potassium carbonate pellets (or crushed, sieved material) were subjected to a "burnoff" period in an oxygen-containing atmosphere at a temperature of about 350°-900° C. for times in the range of about 0.5 to 5 hours.

Following burnoff treatment, the support was warmed to about 200° C. to 250° C., then allowed to cool to about 80°-85° C., at which time the desired alkali metal, and optionally, finely divided stainless steel (designated as SS in Table I), were added. After the alkali metal (and, optionally SS) had been thoroughly contacted with the support, an optional post-treatment was carried out in an inert atmosphere. Thus, the finished catalyst was typically heated to about 200°-250° C. for about 0.25 up to 4 hours in order to ensure a fairly uniform distribution of alkali metal (and any other promoter) on the catalyst support.

The specific details on the preparation of catalysts used in Example II, e.g., die lubricant, burnoff conditions, post-treatment conditions, alkali metal and promoter levels, are summarized in Table I.

                                      TABLE I                                      __________________________________________________________________________     Catalyst Preparation                                                           Support Preparation                                                                          Burnoff    Alkali Metal,                                                                         Promoter,                                                                            Post-Treatment                           Catalyst                                                                            Lubricant, Wt %                                                                         Temp, °C.                                                                     Time, h.                                                                            Wt. %  Wt %  Temp., °C.                                                                    Time, h                            __________________________________________________________________________     A    Graphite, 1.0                                                                           900   0.5  K, 4.5 SS, 4.5                                                                              200   0.25                               B    Stearate, 1.0                                                                           350   3    K, 4.8 None  250   1                                  C    Graphite, 1.0                                                                           None  None K, 2.9 None  230   3-4                                D    Graphite, 1.0                                                                           350   3    K, 2.9 None  250   1                                  E    Graphite, 1.0                                                                           350   3    K, 2.9 None  200   1                                  F    Graphite, 1.0                                                                           350   3    K, 2.9 None  230   3-4                                G    Graphite, 1.0                                                                           350   3    K, 2.9 None  230   1                                  H    Graphite, 1.0                                                                           350   3    K, 2.9 None  230   1                                  I    Graphite, 2.0                                                                           350   3    K, 2.9 None  230   3-4                                J    Graphite, 2.0                                                                           350   3    K, 4.8 None  250   1                                  K    Graphite, 1.0                                                                           350   3    K, 4.8 None  250   1                                  L    Graphite, 1.0                                                                           350   3    Na, 2.5                                                                               None  230   3-4                                M    Marlex ®, 1.0                                                                       450   3    K, 4.5 SS, 4.5                                                                              200   0.25                               N    Graphite, 1.0                                                                           350   3    K, 4.5 SS, 4.5                                                                              250   1                                  O    Graphite, 1.0                                                                           350   3    K, 4.5 SS, 4.5                                                                              200   0.25                               P    Graphite, 1.0                                                                           450   3    K, 4.5 SS, 4.5                                                                              250   1                                  Q    Graphite, 2.0                                                                           450   3    K, 4.5 SS, 4.5                                                                              200   0.25                               R    Graphite, 1.0                                                                           600   3    K, 4.5 SS, 4.5                                                                              250   1                                  S    Graphite, 1.0                                                                           600   3    K, 4.5 SS, 4.5                                                                              250   1                                  T    Graphite, 3.0                                                                           600   3    K, 4.5 SS, 4.5                                                                              200   0.25                               __________________________________________________________________________

Several of the catalyst supports, before K treatment, were analyzed for residual carbon content after the burnoff period. Representative values are presented in Table II.

                  TABLE II                                                         ______________________________________                                         Carbon Content of Pelleted Catalyst Support                                    Burnoff                Carbon Content, Wt %                                    Temp, °C.                                                                         Time Hr.     Initial   Final                                         ______________________________________                                         350       1            1.0       0.8                                           350       3            1.0       0.7                                           350       5            1.0       0.2                                           450       3            1.0       0.3                                           600       3            1.0       0.1                                           ______________________________________                                    

The crush strengths of several pelleted potassium carbonate supports were determined employing a pellet strength tester instrument. The typical crush strength of a 1/8" diameter pellet was found to vary within the range of about 20-30 pounds. This is far superior to the crush strength of granular (about 6 mesh) potassium carbonate, which is only about 3 pounds.

The potassium carbonate pellets were visually inspected both before and after the "burnoff" step. Whereas unoxidized support was uniformly black throughout, the oxidized support was gray on the surface, while the interior portions remained black. Thus, even by visual inspection alone, it is clear that the concentration of carbonaceous compound is less at the surface of the support compared to the concentration of carbonaceous compound in the interior portions of the support. However, upon severe oxidation treatment, such as for example, the treatment to which the support from which catalyst A is prepared (900° C. for 30 minutes), the support evidences no residual carbon content by visual inspection.

EXAMPLE II Dimerization of Propylene

Typically, the dimerization of propylene was carried out in a steam heated 316 stainless steel tubular reactor (1/2"×20"). The catalyst (50 g; density˜1.1 g/mL), bounded above and below by small volumes of glass beads, was heated to the reaction temperature of 150° C. at about 1500 psig and the propylene was pumped into the reactor at a rate of about 120 mL/hr. After about 6 hours of reaction time a sample was taken and analyzed by gas liquid chromatography (glc). Results of numerous propylene dimerization reactions are summarized in Table III.

                  TABLE III                                                        ______________________________________                                         Propylene Dimerization                                                                             Propylene Selectivity to                                                                          4MP1                                    Run No.  Catalyst   Conv., %  4-MP-1, %                                                                               4MP2                                    ______________________________________                                         A. Alkali Metal Promoter Only                                                   1       Control A  3.6       85       12                                       2       Control B  3.9       84       11                                       3       Invention C                                                                               4.9       89       28                                       4       Invention D                                                                               10.9      89       28                                       5       Invention E                                                                               8.6       89       30                                       6       Invention F                                                                               12.2      89       27                                       7       Invention G                                                                               9.3       88       21                                       8       Invention H                                                                               8.1       89       35                                       9       Invention I                                                                               11.0      89       35                                      10       Invention J                                                                               22.6      89       33                                      11       Invention K                                                                               18.0      90       33                                      12       Invention L                                                                               8.7       87       20                                      B. Alkali Metal-Stainless Steel (SS) Promoters                                 13       Control M  6.0       83        9                                      14       Invention N                                                                               20.1      89       26                                      15       Invention O                                                                               11.8      90       37                                      16       Invention P                                                                               14.5      86       13                                      17       Invention Q                                                                               12.7      86       15                                      18       Invention R                                                                               7.4       83        9                                      19       Invention S                                                                               5.5       84       10                                      20       Invention T                                                                               5.6       82        9                                      ______________________________________                                    

All of the "alkali metal promoter only" invention catalysts (catalysts C-L) give improved propylene conversion and improved selectivity to 4-methyl-1-pentene relative to control Catalyst A (no residual carbonaceous compound) and Control Catalyst B (stearate die lubricant vs. graphite die lubricant). In addition, all of the "alkali metal promoter only" invention catalysts produce higher 4-methyl-1-pentene (4-MP-1) to 4-methyl-2-pentene (4-MP-2) ratios than do the control catalysts. Since the separation of 4-MP-1 and 4-MP-2 mixtures is quite difficult, high ratios of 4-MP-1to 4-MP-2 are desirable for the recovery of high purity 4-MP-1.

Several of the alkali metal-stainless steel promoted invention catalysts (Catalysts N-R) give enhanced propylene conversion relative to control catalyst M. All invention catalysts give product selectivities which are comparable to or better than that achieved with the control catalyst. In addition, several of the invention catalysts also provide a significantly increased 4-MP-1 to 4-MP-2 ratio compared to control catalyst M.

Note that the addition of stainless steel to control catalyst M imparts improved catalyst activity compared to control catalysts A and B, but that the invention pelleted potassium carbonate support is required for the high conversions displayed, for example, by catalyst N; the high selectivities displayed, for example, by catalyst O; and the high 4-MP-1 to 4-MP-2 ratios displayed, for example, by catalyst O.

The examples have been provided merely to illustrate the practice of my invention and should not be read so as to limit the scope of my invention or the appended claims in any way. Reasonable variations and modifications, not departing from the essence and spirit of my invention, are contemplated to be within the scope of patent protection desired and sought. 

I claim:
 1. A method for producing a catalyst support which comprises:(a) pelletizing a mixture of potassium carbonate and 0.1 to 10 weight percent of at least one carbonaceous compound selected from the group consisting of: carbon black, charcoal, coconut charcoal, amorphous graphite, and crystallite graphite; wherein said wt. % is based on the total weight of potassium carbonate and the carbonaceous compound; and (b) heating the pelletized product of step (a) in an oxygen-containing atmosphere under conditions suitable to oxidatively remove in the range of 10 to 90% of said carbonaceous compound.
 2. A method in accordance with claim 1 wherein said conditions suitable to oxidatively remove said carbonaceous compound comprise a temperature in the range of 200° to 900° C. for a time in the range of 0.1 to 48 hours.
 3. A method for producing a dimerization catalyst which comprises contacting the support prepared in accordance with claim 1 with at least one elemental alkali metal in an oxygen-free atmosphere at a temperature sufficient to cause the alkali metal to melt.
 4. A method in accordance with claim 3 further comprising heating said dimerization catalyst to a temperature of at least 150° C. for a time in the range of 0.1 to 4 hours.
 5. A catalyst support consisting essentially of:potassium carbonate having a minimum particle size of about 300 microns, a crush strength of at least about 5 pounds and 0.09 to 9 wt. % of at least one carbonaceous compound selected from the group consisting of: carbon black, charcoal, amorphous graphite, and crystallite graphite; wherein said wt. % is based on the total weight of potassium carbonate and carbonaceous compound; and wherein the concentration of said carbonaceous compound is substantially less at the surface of said support than in the interior portions thereof.
 6. A catalyst composition consisting essentially of the catalyst support of claim 5 and 0.1 to 20 wt. % of at least one elemental alkali metal, wherein said wt. % is based on the total weight of said catalyst composition.
 7. A catalyst composition in accordance with claim 6 further consisting essentially of at least one component selected from the group consisting of:elemental cobalt, elemental copper, and finely divided stainless steel.
 8. A catalyst in accordance with claim 6 wherein said at least one elemental alkali metal is elemental potassium. 